SUS 201 Stainless Steel strip
201 Grade stainless steel is an austenitic chromium-nickel-manganese stainless alloy.201 Grade Stainless Steel Cold Rolled Coils Strip(SUS 201 stainless steel) has good formability, corrosion resistance, and fabricability.  It was developed to conserve nickel,In the 201 composition, manganese and nitrogen are partially substituted for nickel.and it is used as an alternative to 301 in some tempered applications.201 offering comparable corrosion resistance and formability to 301 and 304 and has become a viable lower cost alternative to these austenitic grades. Because of 201 's relatively high yield strength in the annealed condition, use of 201 is limited. 201 is generally used in the tempered condition particularly for springs and fasteners. 201 Stainless will retain a comparable ductility to 301 even with the higher yield strength. 201 can be used in many applications because of its wide range of mechanical properties in the annealed and cold worked condition. 201 is non-magnetic in the annealed condition but becomes magnetic as a result of cold working.

Specifications
Thickness: 0.05mm-3.0mm,
Width: 1.5-650mm

Surface
Cold 2D，2B (Matte), BA (4K bright surface, 8K mirror), HL (brushed), DF (sandblasting)

201 Stainless Steel Strip Applications
201 stainless steel strip has good formability and corrosion resistance and this makes it suitable for below applications such as kitchen equipment and catering equipment. 
The good strength ensures suitability in applications such as stainless steel banding straps, clamps, brackets and cable ties. 

Chemical Composition
C ≤ 0.15
Si ≤ 0.75
Mn: 5.5～7.50
Cr: 16.0～18.0
N ≤ 0.25
P ≤ 0.060
S ≤ 0.030
Ni: 0.6-5.50%
C: Half copper 0.8%, High Copper 1.5%

Physical Properties
Tensile Strength: 520MPa
Yield Strength: 275MPa
Elongation Rate: 55 to 60%
Modulus: 29,000,000 psi, Converted is: 203000MPa
Hardness Requirements (Brinell hardness) HRB〈183N/mm²(MPa).
Density: 280lbs/cubic inch (Density 7.93g/cm3)

Equivalent Grades of 201 Stainless Steel Strip