301 Stainless Steel is an austenitic stainless steel capable of attaining very high strengths while maintaining ductility through cold working. Stainless Steel 301 can be used in mould goods. Also it can be quickly hardened by mechanical processing. It has  good weldability. Its wear resistance and fatigue strength are better than that of 304 stainless steel. Compared with 304, its content of Cr and Ni is low. And it has magnetism after cold rolling.

 

301 is non-magnetic in the annealed condition and becomes increasingly magnetic with cold working. This chromium nickel stainless steel alloy provides high strength and good ductility when cold worked. 301 stainless steel is a modification of stainless steel grade 304 with lower chromium and nickel to increase the work hardening range. 301 steel exhibits corrosion resistance comparable to 304. In the cold worked and annealed condition,301 achieves its most optimal resistance to corrosion. It is preferable over 304 in the tempered condition because the higher enlongations (which are attainable at a given strength level) facilitate fabrication.

Chemical Composition(%)

 

Grade   C Mn Si P S Cr Mo Ni N
301 Min 16.0 2.00 10.0
max 0.08 2 0.75 0.045 0.03 18.0 3.00 14.0 0.1

 

Mechanical Properties 

Grade Tensile Strength (MPa) min Yield Strength 0.2% Proof (MPa) min Elongation (% in 50mm) min Hardness
Rockwell B (HR B) max Brinell (HB) max
301 515 205 35% 75 205

 

Classification

301 stainless steel strips can be classified as 301 soft steel strip, 301 medium hard steel strip, 301 hard steel strip. It is determined by its chemical composition and processing technology.

Equivalent Grades of 301 Stainless Steel Strip 

STANDARD UNS JIS WERKSTOFF NR. AFNOR BS GOST EN
SS 301 S30100 SUS 301 1.4310