316/316L Stainless Steel Strip


316/316L Stainless Strip

Stainless steel 316/316L is a chromium nickel austenitic stainless steel containing molybdenum. The molybdenum addition enhances the corrosion resistance over that of 304/304L in halide environments as well as in reducing acids such as sulfuric and phosphoric acid. Type 316L can be dual certified as 316 when the composition meets the lower carbon limit of 316L and the slightly higher strength levels of 316. Type 316L should be specified for welded applications as the low carbon version eliminates chromium carbide precipitation and enhances the corrosion resistance in the as-welded condition.

316/316L stainless steel resists atmospheric corrosion as well as in moderately oxidizing environments. It also resists corrosion in marine atmospheres and has excellent resistance to intergranular corrosion in the as-welded condition. Type 316/316L has excellent strength and toughness at cryogenic temperatures. Type 316/316L is non-magnetic in the annealed condition but may become slightly magnetic as a result of severe cold working.

Propertiesof 316L Stainless Strip in Tempered Conditions

1/16 Hard
Ultimate Tensile Strength: 85 KSI min (585 MPA min)
Yield Strength: (0.2% Offset) 45 KSI min (310 MPA min)
Elongation: 35% Min

1/8 Hard
Ultimate Tensile Strength: 100 KSI min (690 MPA min)
Yield Strength: (0.2% Offset) 55 KSI min (380 MPA min)
Elongation: 25% Min

1/4 Hard
Ultimate Tensile Strength: 125 KSI min (860 MPA min)
Yield Strength: (0.2% Offset) 75 KSI min (515 MPA min)
Elongation: 8% Min

Tempered

 

 

Stainless Steel 316L can be cold rolled to achieve the temper properties required by specific customers and/ or manufacturing requirements. For tempers 1 /2 hard or above consult Ulbrich Technical Services for more information. 

 